| Base material | Cellulose paper (CP) |
| Resin | Phenolic (PF) |
| Formate | IØ 8-590 x approx. 1000 mm |
| Application | Elekrtische Anwendung bei Hochspannung Netzfrequenz |
| Flexural strength perpendicular to layer direction 5.1 MPa min | 100 |
| Compressive strength axial 5.2 MPa min | 80 |
| Adhesion between layers 5.3 MPa min | 70 |
| Dielectric strength perpendicular 6.1 kV/mm min | 9,9 |
| Breakdown voltage parallel 6.1 kV min | 50 |
| Insulation resistance 6.2 MΩ min | 1 |
| Permittivity 48 - 62 Hz 6.2 max | - |
| Permittivity 1 MHz 6.3 max | - |
| Dissipaton factor 48 - 62 Hz 6.3 max | - |
| Dissipaton factor 1MHz 6.3 max | - |
| Themal enduracne 7.1 T.I. min | 120 |
| Water absorption 7.2 mg/cm² max | 10 |
| Density 8.1 g/cm³ | 1,05 - 1,15 |
| Flammability 8.2 Kategorie | - |